Rupture strength of several nickel-base alloys in sheet form

Dance, James H Clauss, Francis J
April 1957

The 100-hour rupture strengths of Inconel X, Inconel 700, Incoloy 901, Refractaloy 26, and R-235 at 1200 and 1350 F. in both the annealed and heat-treated conditions were determined. Inconel 700 had the highest rupture strength at both temperatures; Incoloy 901 was second strongest at 1200 F, and R-235 second strongest at 1350 F. With the exception of Incoloy 901, ductility was low. Photomicrographs show that fractures are through the grain boundaries. Results are compared with published data for other sheet alloys and bar stock.