Adhesive and protective characteristics of ceramic coating A-417 and its effect on engine life of forged Refractaloy-26 (AMS 5760) and cast stellite 21 (AMS 5385) turbine blades

Garrett, Floyd B., Gyorgak, Charles A.
naca-rm-e52l30
1953


The adhesive and protective characteristics of National Bureau of Standards Coating A-417 were investigated, as well as the effect of the coating on the life of forged Refractaloy 26 and cast Stellite 21 turbine blades. Coated and uncoated blades were run in a full-scale J33-9 engine and were subjected to simulated service operations consisting of consecutive 20-minute cycles (15 min at rated speed and approximately 5 min at idle). The ceramic coating adhered well to Refractaloy 26 and Stellite 21 turbine blades operated at 1500 degrees F. The coating also prevented corrosion of the Refractaloy 26, a corrosion-sensitive nickel-base alloy, and of the Stellite 21, a relatively corrosion-resistant cobalt-base alloy. Although the coating prevented corrosion of both alloys, it had no apparent effect on blade life.

An Adobe Acrobat (PDF) file of the entire report:
http://naca.central.cranfield.ac.uk/reports/1953/naca-rm-e52l30.pdf