C. W. MacGregor, N. Grossman
An investigation was conducted to determine the effects of cyclic loading on the mechanical behavior of 24S-T4 and 75S-T6 aluminum alloys and SAE 4130 steel. Specimens of the three materials were subjected to various numbers of prior fatigue cycles both below and above the fatigue limits. Special slow-bend tests were employed to show the effects of prior cycles of fatigue stressing on the transition temperature to brittle fracture for SAE 4130 steel and on the energy-absorption capacity of the aluminum alloys. Micrographic studies were made to observe and measure crack formation and propagation and additional special tests were conducted to supplement the results of the slow-bend tests. These included Charpy impact tests, mirohardness surveys, tension tests, and fretting-corrosion studies.