Axial fatigue tests at zero mean stress of 24S-T and 75S-T aluminum-alloy strips with a central circular hole

Brueggeman, W C (National Bureau of Standards) Mayer, M JR (National Bureau of Standards)
naca-tn-1611
1948


Axial fatigue tests at zero mean stress have been made on 0.032- and 0.064-inch 24S-T and 0.032-inch 75S-T sheet-metal specimens 1/4, 1/2, 1, and 2 inches wide without a hole and with central holes giving a range of hole diameter D to specimen width W from 0.01 to 0.95. No systematic difference was noted between the results for the 0.032-inch and the 0.064-inch specimens although the latter seemed the more consistent. In general the fatigue strength based on the minimum section dropped sharply as the ration D/W was increased from zero to about 0.25. The plain specimens showed quite a pronounced decrease in fatigue strength with increasing width. The holed specimens showed only slight and rather inconclusive evidence of this size effect. The fatigue stress-concentration factor was higher for 75S-T than for 24S-T alloy. Evidence was found that a very small hole would not cause any reduction in fatigue strength.

An Adobe Acrobat (PDF) file of the entire report:
http://naca.central.cranfield.ac.uk/reports/1948/naca-tn-1611.pdf