Nile, Alfred S (Stanford University)
Thirty-three 24ST aluminum-alloy 2- by 2- by 0.10-inch channels, with lengths ranging from 10 to 90 inches were tested at Stanford University in compression to obtain an experimental verification of the theoretical formulas for torsional failure developed by Eugene E. Lundquist of the N.A.C.A. The observed critical loads and twist-axis locations were sufficiently close to the values obtained from the formulas to establish the substantial validity of the latter. The differences between observed and computed results were small enough to be accounted for by small and mostly unavoidable differences between actual test conditions and those assumed in deriving the formulas. Some data were obtained from the shorter specimens regarding the growth of the buckles that resulted in local buckling failure.